Curing property and plywood adhesive performance of resol-type phenol-urea-formaldehyde cocondensed resinsAuthor(s): Masahiko Ohyama; Bunichiro Tomita; Chung-Yun Hse
Source: Holzforschung, Vol. 49: 87-91
Publication Series: Miscellaneous Publication
PDF: View PDF (1.39 MB)
DescriptionThe curing processes and thermal properties of resol-type phenol-urea-formaldehyde cocondensed resins, which were prepared by alkaline treatments of the cocondensed resins once synthesized from UF-concentrate and phenol, were investigated by torsional braid analysis. The resol-type cocondensed resins displayed almost the same curing behaviors and heat-resistance as a commercial resol. Their apparent activation enegies determined by measuring temperature dependence of gel time were almost identical with that of resol, and quite difference from that of UF resin. Their plywood adhesive performances were evaluated with a cyclic 4-hour boil test and a 72 hour boil test. The plywood test results passed the requirements for the JAS special grade structural plywood.
- You may send email to firstname.lastname@example.org to request a hard copy of this publication.
- (Please specify exactly which publication you are requesting and your mailing address.)
- We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
- This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.
CitationOhyama, Masahiko; Tomita, Bunichiro; Hse, Chung-Yun. 1995. Curing property and plywood adhesive performance of resol-type phenol-urea-formaldehyde cocondensed resins. Holzforschung, Vol. 49: 87-91
KeywordsPhenol, urea, formaldehyde, cocondensed resins, resol curing, thermal property, adhesive strength, plywood
- Curing property and plywood adhesive performance of resol-type phenol-urea-formaldehyde cocondensed resins
- Phenol-Urea-Formaldehyde (PUF) co-condensed wood adhesives
- Analysis of curing process and thermal properties of phenol-urea-formaldehyde cocondensed resins
XML: View XML