Source: Wood and fiber science. Vol. 40, no. 2 (2008): Pages 271-278
Publication Series: Miscellaneous Publication
PDF: Download Publication (222 KB)
DescriptionWood-plastic composites (WPCs) continue to make inroads into the decking market. One of the main drawbacks from the consumer’s perspective is that they can fade during weathering. It has been shown that WPCs fade more when exposed to a combination of light and water spray than when exposed only to light. This suggests that the loss of the color-imparting extractives from the wood could be partly to blame for color fade. Pigments are routinely added to only the plastic matrix to combat WPC color fade despite the fact that change in color could be due primarily to changes in the wood component of WPCs. In this study, we investigated two methods of fiber pretreatment in an attempt to improve the color stability of WPCs. The first was to remove water-soluble extractives from wood flour through a series of washes. Washed wood flour was then compounded with high-density polyethylene and injection-molded into test specimens. The second method involved coloring wood flour with either a water-based dye or an oil-based stain. Colored wood flour was also compounded with high-density polyethylene and injection-molded into test specimens. Pigments were added to half of the composites containing colored wood. The composites underwent accelerated weathering in a xenon-arc weathering apparatus, and were monitored for changes in color. Washing wood flour and coloring wood flour with a water-based dye were ineffective for improving composite color stability during weathering. However, coloring wood flour with an oil-based stain resulted in a more color stable WPC.
- We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
- This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.
CitationStark, Nicole M.; Mueller, Scott A. 2008. Improving the color stability of wood-plastic composites through fiber pre-treatment. Wood and Fiber Science. 40(2): 271-278
KeywordsWood-plastic composites, weathering, color, extractives, pigments, dyes, dyeing, accelerated life testing, composite materials, deterioration, color fading, polyethylene, injection molding of plastics, wood flour, wood-plastic materials, stains, staining, wood extractives, HDPE, surface properties, accelerated testing, discoloration, photostabilizers, pigments
- Changes in wood flour/HDPE composites after accelerated weathering with and without water spray
- Feasibility of using saltcedar as a filler in injection-molded polyethylene composites
- Characterization of weathered wood-plastic composite surfaces using FTIR spectroscopy, contact angle, and XPS
XML: View XML