Thermosets as compatibilizers at the isotactic polypropylene film and thermomechanical pulp fiber interphaseAuthor(s): Sangyeob Lee; Todd F. Shupe; Chung Y. Hse
Source: Composite Interfaces, Vol. 15, No. 2?3, pp. 221?230 (2008)
Publication Series: Miscellaneous Publication
PDF: Download Publication (2.3 MB)
DescriptionThe objective of this study was to improve interfacial adhesion properties at the interface of thermomechanical pulp (TMP) fiber and isotactic polypropylene (iPP) using thermoset adhesives such as phenol formaldehyde (PF) and urea formaldehyde (UF). This study also attempted to achieve fiber-to-fiber adhesion using thermoset adhesives before the molten iPP would flow into the fiber web. The fracture surfaces with thermoset adhesive showed identical differences in terms of fracture modes at the interface. An increased TMP fiber failure was observed with increased thermoset quantity at the interface. Using one percent resin content of weight fraction of TMP fiber handsheet, the tensile strength properties increased almost two fold higher than the strength of control samples. Additional adhesive contents of three and five percent showed gradual strength enhancement. However, the enhanced strength was statistically insignificant. UF resin showed slightly better strength performance over PF resin. This result may be caused by solid contents and additional pigments of resins.
- You may send email to email@example.com to request a hard copy of this publication.
- (Please specify exactly which publication you are requesting and your mailing address.)
- We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
- This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.
CitationLee, Sangyeob; Shupe, Todd F.; Hse, Chung Y. 2008. Thermosets as compatibilizers at the isotactic polypropylene film and thermomechanical pulp fiber interphase. Composite Interfaces, Vol. 15, No. 2?3, pp. 221?230 (2008)
KeywordsThermomechanical pulp (TMP), thermoset resins, polypropylene (PP), laminates, interfacial properties.
Plasma enhanced modification of TMP fiber and its effect on tensile strength of wood fiber/PP composite
- Wetting behaviors of phenol- and urea-formaldehyde resins as compatiblizers
- Thermomechanical pulp fiber surface modification for enhancing the interfacial adhesion with polypropylene
XML: View XML