Bond quality of phenol-based adhesives containing liquefied creosote-treated woodAuthor(s): Chung-Yun Hse; Feng Fu; Hui Pan
Source: Conference Proceedings Paper In: Hse, Chung-Yun; Jiang, Zehui; Kuo, Mon-Lin, eds. Advanced biomass science and technology for bio-based products: Proceedings of the meeting: 2007 May 23-25; Beijing, China. People’s Republic of China: Chinese Academy of Forestry: 87-95.
Publication Series: Miscellaneous Publication
Station: Southern Research Station
PDF: Download Publication (1.35 MB)
Liquefaction of spent creosote-treated wood was studied to determine the technological practicability of its application in converting treated wood waste into resin adhesives. A total of 144 plywood panels were fabricated with experimental variables included 2 phenol to wood (P/W) ratios in liquefaction, 6 resin formulations (3 formaldehyde/liquefied wood (F/LW) ratios × 2 replications), 6 glue applications (2 glue spreads × 3 assembly times), and 2 panel replications. Average shear strength (235.6 psi) and wood failure (70.5%) for resin adhesives prepared from liquefied wood at P/W ratio of 2.0 were significantly higher than the shear strength (184.7 psi) and wood failure (53.1%) for that at P/W ratio of 1.5. On average, F/LW ratio of 2.25 yielded substantially lower shear strength and wood failure than that of F/LW ratios of 2.0 and 1.75. Differences in shear strength and wood failure between F/LW ratios of 2.0 and 1.75 were not significant. However, it is interesting to note that F/LW ratio interacted with P/W ratio to affect wood failure, but not shear strength. As shown in Fig. 2, at P/W ratio of 1.5, the F/LW ratio of 2.0 yielded the highest wood failure and the F/LW ratio of 2.25 resulted in the lowest wood failure. On the contrary, at P/W ratio of 2.0, the F/LW ratio of 2.25 resulted in highest wood failure and the F/LW ratio of 2.0 yielded the lowest wood failure. On the basis of wood failure, the resins prepared from liquefied wood at P/W ratio of 2., reacted at F/LW ratio of 2.25, and applied the glue at the rate of 90 pounds per 1000 square ft of double glue line met the standard of vacuum pressure soak cycle for exterior glueline (PS-1-66). Nevertheless, the first attempt to formulate a phenol-based adhesive made from liquefied creosote-treated wood produced encouraging results. With additional studies of resole formation and glue mix formulations, it is anticipated that a resin adhesive from liquefied creosote-treated wood with improved bond quality can be developed.
- You may send email to firstname.lastname@example.org to request a hard copy of this publication.
- (Please specify exactly which publication you are requesting and your mailing address.)
CitationHse, Chung-Yun;Fu, Feng; Pan, Hui. 2009. Bond quality of phenol-based adhesives containing liquefied creosote-treated wood. In: Hse, Chung-Yun; Jiang, Zehui; Kuo, Mon-Lin, eds. Advanced biomass science and technology for bio-based products: Proceedings of the meeting: 2007 May 23-25; Beijing, China. People’s Republic of China: Chinese Academy of Forestry: 87-95.
- Liquefaction of the Used Creosote-Treated Wood in the Presence of Phenol and Its Application to Phenolic Resin
- Physical and mechanical properties of bio-composites from wood particles and liquefied wood resin
- Preparation and Characterization of Novolak Phenol Formaldehyde Resin from Liquefied Brown-Rotted Wood
XML: View XML