Modifications of surfactant distributions and surface morphologies in latex films due to moisture exposureAuthor(s): Guizhen H. Xu; Jinping Dong; Steven J. Severtson; Carl J. Houtman; Larry E. Gwin
Source: Journal of physical chemistry. B. Vol. 113, no. 30 (July 30, 2009): pages 10189-10195.
Publication Series: Miscellaneous Publication
View PDF (370.33 KB)
DescriptionMigration of surfactants in water-based, pressure-sensitive adhesive (PSA) films exposed to static and cyclic relative humidity conditions was investigated using confocal Raman microscopy (CRM) and atomic force microscopy (AFM). Studied PSA films contain monomers n-butyl acrylate, vinyl acetate, and methacrylic acid and an equal mass mixture of anionic and nonionic nonylphenol ethoxylate emulsifiers. A leveling of surfactant concentration distributions is observed via CRM after films stored at 50% relative humidity (RH) are exposed to a 100% RH for an extended time period, while relatively small increases in surface enrichment occur when films are stored at 0% RH. Use of CRM for binary mixtures containing anionic or nonionic surfactant and latex that has undergone dialysis to remove nonpolymeric components indicates that surfactant-polymer compatibility governs to a great extent surface enrichment, but not changes observed with humidity variations. AFM images show that upon drying latex coatings, surfactant and other additives collect in large aggregation regions, which protrude from film surfaces. These structures are absent at high humidity, which appears to result from lateral spreading across the polymer surface. When humidity is reduced, aggregation regions reform but appear to be smaller and more evenly dispersed, and by cycling humidity between 0 and 100% RH, interfacial enrichment can be seen to diminish. Presented results provide greater insights into the distribution behavior of surfactants in latex films and potential mechanisms for observed issues arising for these systems.
- We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
- This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.
CitationXu, Guizhen H.; Dong, Jinping; Severtson, Steven J.; Houtman, Carl J.; Gwin, Larry E. 2009. Modifications of surfactant distributions and surface morphologies in latex films due to moisture exposure. Journal of physical chemistry. B. Vol. 113, no. 30 (July 30, 2009): pages 10189-10195.
KeywordsSurface active agents, glue, adhesion, adhesives, testing, pressure-sensitive adhesives, latex, vinyl acetate, methacrylic acid, moisture, humidity, coatings, atomic force microscopy, AFM, confocal Raman microscopy, CRM, n-butyl acrylate, bond strength, bonding, nonylphenyl ethoxylate emulsifiers, moisture content, polymers, polymerization
- Characterizing the distribution of nonylphenol ethoxylate surfactants in water-based pressure-sensitive adhesive films using atomic-force and confocal Raman microscopy
- Surface Enrichment by Conventional and Polymerizable Sulfated Nonylphenol Ethoxylate Emulsifiers in Water-Based Pressure-Sensitive Adhesive
- Properties of water-based acrylic pressure sensitive adhesive films in aqueous environments
XML: View XML