The effects of different silane crosslinking approaches on composites of polyethylene blends and wood flourAuthor(s): Craig M. Clemons; Ronald C. Sabo; Kolby C. Hirth
Source: Journal of applied polymer science. Vol. 120, no. 4 (May 15, 2011): p. 2292–2303.
Publication Series: Scientific Journal (JRNL)
View PDF (1.25 MB)
DescriptionThough silane chemistry has been used to crosslink unfilled polyethylene for many years, such crosslinking has only been recently applied to wood plastic composites to improve properties such as creep resistance. However, the presence of wood significantly changes the silane chemistry and a greater understanding is necessary for optimal processing and performance. We investigated three different approaches of adding silane and peroxide during reactive extrusion of wood-plastic composites were investigated and compared to their unfilled counterparts. Up to 2 grams of a 20:1 solution of vinyltrimethoxysilane and dicumyl peroxide by weight were added per 100 grams of plastic. Low density polyethylene, high density polyethylene, and a blend of the two were investigated as matrices in composites containing approximately 25% wood flour. The unfilled plastics crosslinked efficiently and little premature crosslinking occurred during processing. Though only modest improvements in tensile strengths were found in unfilled plastics, the notched Izod impact energy of unfilled HDPE improved nearly 600% when crosslinked. Unlike the unfilled plastics, most of the crosslinking of the composites occurred during processing. This resulted in high viscosities and processing difficulties, negating some of the advantages of a separate crosslinking step and limiting the amount of crosslinking possible. Some reinforcement of the plastics by the wood flour was achieved when sufficient crosslinking solution was added. Adding crosslinking solution also and greatly increased reverse-notched impact energies. The differences between the approaches for preparing the crosslinked composites appeared to largely be a matter of efficiency in terms of the amount of crosslinking solution required to affect processing and performance. The most efficient approach was a two-step procedure where the silane was first grafted to the plastic and then wood flour was compounded with the grafted silane in a second step.
- We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
- This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.
CitationClemons, Craig M.; Sabo, Ronald C.; Hirth, Kolby C. 2011. The effects of different silane crosslinking approaches on composites of polyethylene blends and wood flour. Journal of applied polymer science. Vol. 120, no. 4 (May 15, 2011): p. 2292–2303.
KeywordsComposite materials, mechanical properties, injection molding of plastics, thermoplastic composites, plastics, extrusion, wood-plastic composites, silane, testing, extrusion process, crosslinking, polyethylene, wood flour, materials, creep, peroxides, dicumyl peroxide, impact testing, viscosity, recycled products, wood-plastic materials, biocomposites, HDPE, high density polyethylene, vinyltrimethoxysilane, strength, tensile strength, Izod test, reactive extrusion
- Effects of silane on the properties of wood-plastic composites with polyethylene-polypropylene blends as matrices
- Elastomer modified polypropylene–polyethylene blends as matrices for wood flour–plastic composites
- Evaluation of various fire retardants for use in wood flour--polyethylene composites
XML: View XML