Veneer-reinforced particleboard for exterior structural composition boardAuthor(s): Chung-Yun Hse; Todd F. Shupe; Hui Pan; Fu Feng
Source: Forest Products Journal 62(2):139-145
Publication Series: Scientific Journal (JRNL)
Station: Southern Research Station
PDF: Download Publication (298.15 KB)
DescriptionTwo experiments were performed to determine the physical and mechanical characteristics of panels consisting of a veneer face and a particleboard core composed of mixed wood particles/powdered-recycled polyethylene (PE) bag waste (MWP) using urea-formaldehyde (UF) resin as a binder. The addition of 25 percent powdered-recycled PE bag waste to the MWP panels did not adversely affect nonaged bonding strength but did result in substantial improvement in internal bond (IB) retention after a 24-hour water soak and improved dimensional stability. Average MWP panel IB retention was more than 300 percent higher than the IB retention of wood particle (WP) panels and MWP thickness swell and linear expansion were 70 and 44 percent lower, respectively, than the values for WP panels. For the veneer overlay composite, the mean modulus of rupture (MOR) parallel to the surface grain veneer (MORjj) was lowest (3,668.2 pounds per square inch [psi]) for panels with two veneers cross-laminated on each face over a WP core. Conversely, MORjj was greatest (8,535.6 psi) for panels with single 1/8-inch veneers on each face over an MWP core. However, the large percentage of shear failure when stressed parallel to face veneer grain hindered an accurate determination of true MOR. As expected, all specimens tested in bending parallel to the surface grain of the veneers resulted in higher modulus of elasticity (MOE) than those tested perpendicular to the grain. For a single veneer overlay on each face, it is interesting to note that thinner veneers (i.e., 1/8 in.) resulted in higher MOE than thicker veneers (i.e., 3/16 in.).
- You may send email to email@example.com to request a hard copy of this publication.
- (Please specify exactly which publication you are requesting and your mailing address.)
- We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
- This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.
CitationHse, Chung-Yun; Shupe, Todd F.; Pan, Hui; and Feng, Fu. 2012. Veneer-reinforced particleboard for exterior structural composition board. Forest Products Journal. 62(2):139-145.
- Exterior structural composite panels with southern pine veneer faces and cores of southern hardwood flakes
- Determining tensile properties of sweetgum veneer flakes
- Effects of density, cellulose nanofibrils addition ratio, pressing method, and particle size on the bending properties of wet-formed particleboard
XML: View XML