    Author(s): Yibin Xue; David Veazie; Cindy Glinsey; Meagan Wright; Roger M. Rowell
    Date: 2003
    Source: Seventh International Conference on Woodfiber-Plastic Composites (and other natural fibers), May 19-20, 2003 ... Madison, Wisconsin, USA. Madison, WI : Forest Products Society, 2003: Pages 339-343
    Publication Series: Miscellaneous Publication
    PDF: View PDF  (169 KB)

    Description

    Woodfiber-thermoplastic composites (WPC) have received considerable attentions from the forest product industry for civil engineering applications due to its superior properties over wood and plastics alone. Particularly WPCs can be easily fabricated using traditional plastic processing techniques. The major limitation in the applications of WPCs is the poor understanding of their mechanical properties and especially the environmental impacts on these properties. The aim of this research is to systematically study the mechanical properties of aspen-fiber polypropylene composites (APCs), evaluate the typical temperature and humidity influences on the mechanical properties of APCs, and such find an optimal composition of APCs for high mechanical reliability and long life span in service conditions. This was accomplished by examining APCs of 30 and 50 weight percent wood fiber contents with/without 2 wt. % maleic anhydride grafted polypropylene MAPP additives. Specimens of these specially selected APCs were exposed for 7,000 hours to four temperature and moisture conditions, typically experienced by structures in domestic housing industry: 1. hot/dry (Arizona), 2. hot/wet (Florida), 3. cold/dry (Montana), and 4. cold/wet (Wisconsin). Tensile and flexural tests according to ASTM specifications were used to evaluate the mechanical properties of these APCs after conditioning. Especially flexural strengths after conditioning were reported here at room, near zero (4°C), and elevated (40°C) temperatures. Large reductions in both tensile and flexure strengths of APCs were observed after 7,000 hours ageing at all four ageing conditions.

    Publication Notes

    • We recommend that you also print this page and attach it to the printout of the article, to retain the full citation information.
    • This article was written and prepared by U.S. Government employees on official time, and is therefore in the public domain.

    Citation

    Xue, Yibin; Veazie, David; Glinsey, Cindy; Wright, Meagan; Rowell, Roger M. 2003. Mechanical properties of wood fiber composites under the influence of temperature and humidity. Seventh International Conference on Woodfiber-Plastic Composites (and other natural fibers), May 19-20, 2003 ... Madison, Wisconsin, USA. Madison, WI : Forest Products Society, 2003: Pages 339-343

    Keywords

    Wood fiber composites, mechanical properties, temperature, humidity